Specifications
CAS NO: 9002-88-4
HS Code: 39012000
Apperance: granule&pellets
High Quality LLDPE Recycled Granules
1, LLDPE film grade
|
Tests |
Value |
Unit |
|
Melt Flow Rate (MFR) |
2.0±0.4 |
g/10min |
|
Density |
920±2 |
Kg/cm3 |
|
Tensile Strengthat Yield |
8 |
Mpa ≥ |
|
Tensile Strengthat Break |
12 |
Mpa ≥ |
|
haze |
15 |
%≤ |
|
Packing |
In 25 kg PP woven bags,20MT/20’FCL
|
2, LLDPE for Master Batch Use
|
Tests |
Value |
Unit |
|
Melt Flow Rate (MFR) |
20 |
g/10min |
|
Density |
0.924 |
g/cm3 |
|
Tensile Strength |
MD12 |
Mpa |
|
TD 10 |
|
Elongation at Yield |
13 |
% |
|
Elongation at Break |
200 |
|
Dark Drop Impact |
105 |
g |
|
Brittle Temperature(F 50) |
-70 |
°C |
|
Vicat Softening Point |
90 |
°C |
|
Packing |
In 25 kg PP woven bags,20MT/20’FCL
|
3, LLDPE Powder Rotational Molding Grade for Tank Use
|
Tests |
Value |
Unit |
|
Melt Flow Rate (MFR) |
3.2 |
g/10min |
|
Density |
0.939 |
g/cm3 |
|
Melting Point |
127 |
°C |
|
Tensile Yield Strength |
21 |
Mpa |
|
Tensile Strength at Break |
28 |
Mpa |
|
Elongation at Break |
1,100 |
% |
|
Flexural Modulus |
750 |
Mpa |
|
Brittle Temperature |
<-60 |
°C |
Application
1 Fiber (Carpet, Textiles, Upholstery, etc.)
2 Film (Shopping bags, casting film, multilayer film, etc.)
3 Blow Molding (Medical & Cosmetic container, Lubricant & Paint container, etc)
4 Extrusion Molding (Sheet, Pipe, Wire & Cable, etc.)
5 Injection Molding (Automotive, Electronic, Construction, House wares, Furniture, Toys, etc.)