ABS is a terpolymer of three monomers: acrylonitrileA), butadiene (B) and styrene (S). The relative content of the three monomers can be changed at will to make various resins. ABS plastic has the common properties of three components. A makes it resistant to chemical corrosion, heat resistance, and has a certain surface hardness, B makes it have high elasticity and toughness, and S makes it have the processing and molding characteristic of thermoplastics and improve electrical properties. performance. Therefore, ABS plastic is a kind of "tough, hard and rigid" material with easy-to-obtain raw materials, good comprehensive performance, low price and wide range of uses.
Properties:
1.Stable shrinkage, good dimensional stability, low warpage
2.Good processability
3.Balance mechanical properties
4.Good exterior, no need to be plated, sprayed
5.Flame resistant
Properties
|
Test Method
|
Test Condition
|
Units
|
Typical Values
|
Physical
|
Melt Flow Rate
|
ASTM D-1238
|
220oC, 10Kg
|
g/10min
|
-
|
Specific Gravity
|
ASTM D-792
|
23oC
|
g/cm3
|
1.03
|
Ash
|
-
|
800oC,30min
|
%
|
-
|
Mechanical
|
Tensile Strength
|
ASTM D-638
|
50mm/min
|
MPa
|
46
|
Elongation at Break
|
ASTM D-638
|
50mm/min
|
%
|
14
|
Flexural Strength
|
ASTM D-790
|
2mm/min
|
MPa
|
62
|
Flexural Modulus
|
ASTM D-790
|
2mm/min
|
MPa
|
1800
|
Impact Strength, IZOD non-notched
|
ASTM D-256
|
23oC
|
KJ/m2
|
-
|
|
|
-30oC
|
KJ/m2
|
-
|
Impact Strength, IZOD notched
|
ASTM D-256
|
23oC
|
KJ/m2
|
17
|
|
|
-30oC
|
KJ/m2
|
-
|
Thermal
|
Heat Deflection Temp.
|
ASTM D-648
|
1.8Mpa
|
oC
|
93
|
|
|
0.45Mpa
|
oC
|
98
|
Others
|
Mold Shrinkage
|
ASTM D-955
|
23oC
|
%
|
0.6-0.9
|
Flammability
|
UL94
|
1/16"
|
|
HB
|
Tip: The technical data sheet is for reference only. We supply the OEM service per your request.
|
|
|